HGH3030

HGH3030焊接性能：合金焊接性能优良，可进行氩弧焊、点焊、缝焊和钎焊。氩弧焊时熔池流动性和成形性能均良好，裂纹倾向性小；接触焊时有较宽的规范参数范围。该合金可与1Cr18Ni9Ti、GH1140、GH3039、GH3044、GH3128等合金组合进行焊接。HGH3030化学成分（%）CCrNiTiAlFeMnSiPS不大于≤0.1219.0～22.0余0.15-0.350.151.50.70.80.030.02HGH3030手工氩弧焊（对接）规范厚度/mm焊前状态焊丝电流/A电压/V气体流/(L/min)钨极直径/mm牌号直径/mm1.0固溶HGH30301.0-1.640-7010-154-61.61.51.6-2.060-9010-155-72.01.81.6-2.070-11010-156-82.0HGH3030不加焊丝的自动钨极氩弧焊（对接）规范厚度/mm焊前状态电流/A电压/V焊速/(m/min)气体流量/(L/min)背面气体流量/(L/min)钨极直径/mm焊嘴直径/mm0.8固溶，机械抛光100-12010-120.710-122-33.018-201.5120-16010-120.37-0.412-143-43.018-201.8150-18010-120.412-143-43.018-20HGH3030固溶状态缝焊规范厚度/mm滚盘宽度/mm规范参数上下电流/A焊接时间/s休止时间/s焊接速度/(m/min)电极压力/N1.0+1.05.05.065000.160.100.653951.3+1.44.0-5.04.0-5.066000.120.100.463751.4+1.54.0-5.07.068000.120.100.469651.4+1.74.0-5.07.075000.160.140.469651.5+1.74.5-5.54.5-5.578000.160.120.469651.5+1.55.55.077000.180.140.566701.7+1.74.54.580000.160.140.46695HGH3030各种焊接接头的力学性能焊接方法接头方式厚度/mm焊前状态焊后状态焊丝牌号接头强度强度系数/%焊点强度/kNθ/℃σb/MPa手工氩弧焊对接1.01.5固溶未处理HGH303020688～760100-800199100-90088--自动氩弧焊对接1.5固溶未处理不加焊丝2065495-70039798.7-缝焊搭接1.01.7固溶未处理-20702～818100-800118--90088--点焊搭接1.5固溶未处理-20--11.7800--2.94900--1.96